SG 166 GM has a viscosity suitable for brush application.
Cure at room temperature, a post-cure is required before release.
Excellent thermal resistance after post-cure.
Good abrasion resistance.
Recommended for manufacturing of mould with a service temperature of 130°C max.

Advantages
– Late overlay of gelcoat.
– Less print of fibers
– Very good adhesion between gelcoat and laminate.

Post curing cycles
Apply the same post-cure cycle as the one recommended for the resin used in the laminate.
A minimum of 12 h at 60°C is generally required before release from the pattern. After release, complete gradually the post-cure with higher temperature.

Laminating
The laminate can start when the gel is still tacky, or later if the gel has been overlay by a surface veil as Armstrim 50, in order to create a mechanical key.
Aluminium powder put directly

The post Epoxy Gel-coat – High Temp. 148°C – SG 166 GM / SD 902 appeared first on ALPHA COMPOSITION.

Curing temp 130C

The post CARBON PREPREG / 400GSM / TW / 12K / 1000mm/ High Curing Temp 130C appeared first on ALPHA COMPOSITION.

Curing temp 130C

The post CARBON PREPREG / 200GSM / TW / 3K / 1000mm / High Curing Temp 130C appeared first on ALPHA COMPOSITION.

This is an epoxy resin formulation designed for manufacturingcarbon fiber and glass fiber prepreg without solvent, and is suitable forvarious composite materials molding.

The post CARBON PREPREG / FORGED / 1000MM / HIGH CURING TEMP 130C appeared first on ALPHA COMPOSITION.

The post E GLASS WOVEN ROVING (EWR) 400GSM 1000MM WIDTH appeared first on ALPHA COMPOSITION.

The post F1 18 mm 88GSM / Spread Tow / PW / 1000 mm appeared first on ALPHA COMPOSITION.

The post 300GSM / PW / Kevlar Tape / 50 mm appeared first on ALPHA COMPOSITION.

ผ้าไฟเบอร์กลาส เบอร์ 160 EWP (E glass)

The post GLASS FIBER 160 GSM 1000MM WIDTH appeared first on ALPHA COMPOSITION.